Effect of glaze on relative translucency of B, C color IPS e.max LT core material

ZHANG Liang¹,FENG Lu²,ZHAO Chunpeng³, SUN Ting⁴

Author information +

History +

Abstract

Objective To evaluate the effect of glaze on relative translucency of B, C color IPS e.max LT core material.Methods Disc-shaped base material IPS e.max LT samples which were 0.3mm and 0.5 mm thick were prepared and divided into eight groups by color number B1, B2, B3, B4, C1, C2, C3, C4, n=5. 0.3 mm-thick dentin porcelain of the same color as the base material was decorated over the surface. Finally, all the samples were glazed and sintered. Relative translucency was determined using a spectral colorimeter and statistically analyzed.Results Analysis results of samples of color B and C showed that thickness was a significant factor for their relative translucency (P<0.05). Using the same color, relative translucency of 0.8 mm groups was higher than that of 0.6 mm group (P<0.05). For samples of 0.6 mm, glazing with color B significantly decreased relative translucency (P<0.05), but had no significant effect on samples of 0.8 mm (P>0.05)except group B4. For color C, glazing had a significant effect on relative translucence of groups of 0.6 mm excepted C3 groups (P<0.05). For groups of 0.8 mm, glazing showed significant effect on C1 and C4 (P<0.05), but not on C2 and C3 (P>0.05).Conclusions The thickness ratio of core materials to dentine porcelain contributes to match color and relative translucency between all-ceramic restoration and natural teeth. Glaze can improve the transparency of all-ceramic restorations their aesthetic effect.

Key words

dentine porcelain / color series / relative translucency / glaze

Cite this article

EndNote

Ris (Procite)

Bibtex

Download Citations

ZHANG Liang,FENG Lu,ZHAO Chunpeng, SUN Ting. Effect of glaze on relative translucency of B, C color IPS e.max LT core material[J]. Medical Journal of the Chinese People Armed Police Forces. 2017, 28(1): 43-46

References

[1] 靳海立,贾骏,邓再喜,等.饰核瓷厚度比对IPS e.max全瓷冠透光度的研究[J]. 中国美容医学, 2015, 22(24): 49-52.
[2] 朴国滨, 赵冰松, 石旭旭. 牙本质比色对铸瓷修复体临床精确选色的意义[J]. 中国组织工程研究, 2014, 18(12): 1889-1894.
[3] Sun T, Shao L Q, Ai J, et al. Relative Translucency of IPS e.max LT Core Materials After Veneeringand Glazing[J]. Key Eng Mater, 2012, 492: 358-361.
[4] 张良,冯露,赵春鹏,等. A、D色系IPS e.max LT底层材料相对透明率的影响因素[J].武警医学,2016,27(9):920-923.
[5] 丁玉梅,宋炜,胡海波.IPS e.max Press全瓷冠对上颌变色前牙遮色效果的研究[J].临床口腔医学杂志, 2014, 30(10): 615-616.
[6] 汪琦瑛,顾斌,温宁,等.四种新型牙科基底瓷材料透射率的对比研究[J].军事医学,2014,38(7): 563-564.
[7] Shao L Q, Sun T, Zhou S Y, et al. Contrast ratios and chromatic value of IPS e.max LT framework materials[J]. Key Eng Mater, 2012, 492: 354-357.
[8] Shao L Q, Wang L L, Liu Q, et al. Measuring the infinite optical thickness of dentine porcelain of the IPS e.max[J]. Key Eng Mater, 2012, 492: 349-353.
[9] Nakamura T, Saito O, Fuyikawa J, et al. Influence of abutment substrate and ceramic thickness on the color of heat-pressed ceramic crowns[J]. Oral Rehabil, 2002, 29(6): 805-809.
[10] Zhou S Y, Shao L Q, Wang L L, et al. Masking ability of IPS e.max all-ceramics system of HO series[J]. Key Eng Mater, 2012, 512-515: 1784-1787.
[11] Sun T, Shao L Q, Wang Y L, et al. Affection of post-core materials on the resultant color of lithium disilicate ceramic restorations[J]. Key Eng Mater, 2012, 512-515: 1761-1764.
[12] Shao L Q, Sun T, Gan Y N, et al. Relative translucency of dental lithium disilicate ceramic restorations[J]. Key Eng Mater, 2012, 512-515: 1775-1778.
[13] 熊芳,巢永烈,朱志敏.瓷层厚度比和瓷粉混合比对饰面瓷半透性的影响[J].实用口腔医学杂志,2008, 24(4): 482-487.
[14] 徐晗,杨瑛, 张根香.核瓷和体瓷厚度对IPS e.max全瓷修复体颜色的影响[J].实用口腔医学杂志, 2011, 27(5): 610-613.
[15] Turner K A, Weinstein A B, Eames W B, et al. Nutural glaze versus overglaze in ceramo-metal restorations[J]. J Ga Dent Assoc, 1997, 50(3): 22-24.
[16] Cook P A, Griswold W H, Post A C. The effect of superficial colorant and glaze on the surface texture of vacuum-fired porcelain[J]. J Prosthet Dent, 1984, 51(4): 476-484.
[17] Griggs J A, Thompson J Y, Anusavice K J. Effect of flaw size and auto-glaze treament on porcelain strength[J]. J Dent Res, 1996, 75(6): 1414-1417.
[18] Aksoy G, Polat M, et al. Effect of various treament and glazing(coating)techniques on the roughness and wettability of ceramic dental restorative surfaces[J]. Colloids Surf B Biointerfaces, 2006, 53(2): 254-259.
[19] Barghi N, Alexander L, Draugh R A. When to glaze--an electron microscope study[J]. J Prosthet Dent, 1976, 35(6): 648-653.
[20] 马桂芳,赵鑫,王迎婕, 等.不同打磨及上釉方法对烤瓷表面性状的影响[J].实用口腔医学杂志, 2008, 24(2): 202-204.
[21] Dalkiz M, Sipahi C, Beydemir B. Effect of six surface treatment methods on the surface roughness of low-fusing and an ultra low-fusing feldpathic ceramic material[J]. J Prosthodont, 2009, 18(2): 217-222.
[22] Heffernan M J, Aquilino S A, Diaz-Amold A M, et al. Relative translucency of six all-ceramic systems. Part II: Core and veneer materials[J]. J Prosthet Dent, 2002, 88(1): 10-15.
[23] 罗媛,罗娟,周军,等.IPS e.max Press全瓷冠用于前牙修复:边缘适合度及颜色匹配随访[J].中国组织工程研究, 2015, 19(25):4017-4021.
[24] 孙雪丹.IPS e.max CAD LT低度透明瓷块修复后牙缺损的临床效果观察[J].口腔医学,2013,33(4): 251-253.